Simon Hope | Crown Kryo 2mm Parting Tool
Crown CRYO 2mm Parting Tool
Length: 280mm, 2mm wide thin parting tool. These tang tools are specially fixed into a
16mm round bar. A special metal liquid is used to set them firmly in place. They can then be used in the red quick release head or 16,5mm grub screw handle.
The two main crystals in tooling steel are the larger and softer austenite and the smaller, more stable martensite. Through heat treatment, we look to transform the austenite to martensite to produce steel with good wear
characteristics and an amount of
ductile properties.
When combined with a good quality heat treatment, the cryogenic process greatly enhances the austenitic transformation. Also at these extreme temperature of -301ºF (-185ºC), fine ‘eta’ carbides are formed within the carbon structure. Growing very slowly and only at these very low temperatures, ‘eta' carbides are extremely small and act as a ‘filler’ between the other crystals in the metal.
The combined effect of the cryogenic processing is to produce a refined crystal structure in your hand tool that will give a lifetime's service by producing a blade that will retain its edge longer and give a superior ‘feel’ in use.
Product Information
Product Information
Shipping & Returns
Shipping & Returns
Simon Hope | Crown Kryo 2mm Parting Tool
Simon Hope | Crown Kryo 2mm Parting Tool
Crown CRYO 2mm Parting Tool
Length: 280mm, 2mm wide thin parting tool. These tang tools are specially fixed into a 16mm round bar. A special metal liquid is used to set them firmly in place. They can then be used in the red quick release head or 16,5mm grub screw handle.
The two main crystals in tooling steel are the larger and softer austenite and the smaller, more stable martensite. Through heat treatment, we look to transform the austenite to martensite to produce steel with good wear
characteristics and an amount of
ductile properties.
When combined with a good quality heat treatment, the cryogenic process greatly enhances the austenitic transformation. Also at these extreme temperature of -301ºF (-185ºC), fine ‘eta’ carbides are formed within the carbon structure. Growing very slowly and only at these very low temperatures, ‘eta' carbides are extremely small and act as a ‘filler’ between the other crystals in the metal.
The combined effect of the cryogenic processing is to produce a refined crystal structure in your hand tool that will give a lifetime's service by producing a blade that will retain its edge longer and give a superior ‘feel’ in use.
$92.48
Simon Hope | Crown Kryo 2mm Parting Tool—
$92.48
Product Information
Product Information
Shipping & Returns
Shipping & Returns
Description
Crown CRYO 2mm Parting Tool
Length: 280mm, 2mm wide thin parting tool. These tang tools are specially fixed into a 16mm round bar. A special metal liquid is used to set them firmly in place. They can then be used in the red quick release head or 16,5mm grub screw handle.
The two main crystals in tooling steel are the larger and softer austenite and the smaller, more stable martensite. Through heat treatment, we look to transform the austenite to martensite to produce steel with good wear
characteristics and an amount of
ductile properties.
When combined with a good quality heat treatment, the cryogenic process greatly enhances the austenitic transformation. Also at these extreme temperature of -301ºF (-185ºC), fine ‘eta’ carbides are formed within the carbon structure. Growing very slowly and only at these very low temperatures, ‘eta' carbides are extremely small and act as a ‘filler’ between the other crystals in the metal.
The combined effect of the cryogenic processing is to produce a refined crystal structure in your hand tool that will give a lifetime's service by producing a blade that will retain its edge longer and give a superior ‘feel’ in use.